PENGARUH PENAMBAHAN KAWAT BENDRAT DAN SERBUK KACA TERHADAP KUAT TEKAN PADA PAVING
Keywords:
Paving, Bendrat Wire, Glass, Compressive StrengthAbstract
Some requirements for paving must have physical properties according to SNI 03-0691-1996 regarding paving, namely compressive strength, wear resistance, and absorption. Efforts to improve these properties can be done by adding fiber to the mixture. The use of glass waste and bendrat wire in partial replacement of fine aggregate is expected to be an alternative to various problems in the construction and environmental world. According to (Soroushian & Bayasi, 1987) the basic idea of adding fiber is to provide reinforcement in concrete with steel fibers that are evenly distributed into the concrete mix which can prevent premature cracks in the concrete, either due to heat of hydration or due to loading, so that expected to be able to increase ductility, abrasion resistance, compressive strength, tensile strength, flexural strength, resistance to shrinkage, fracture and peeling. The compressive strength of standard paving already has good strength, with the addition of glass waste and bendrat wire as fine aggregate, it is expected to be able and further increase the compressive strength of the paving. From the results of research and testing, it can be seen that the effect of adding variations in the mixture of 0%, 5%, 10%, and 15% bendrat wire and glass powder to the compressive strength of paving can increase the compressive strength of concrete by 36.26 Mpa, 46.12, respectively. Mpa, 50.15 Mpa and 55.66 Mpa. The addition of bendrat wire and paving glass powder can increase the value of the compressive strength of paving and is recommended as an additional fiber for paving, with the addition of bendrat wire and glass powder 15% with a percentage increase of 10.2%.
Downloads
References
Faisal Ananda1, M. Z 2016, Oktober. Pengaruh Penambahan Serat Ijuk dan Kawat Bendrat. Invotek, 6, 68-72.
Fauzi, M. R 2020. Pengaruh Limbah Fragmen Kaca Sebagai Subtitusi Sebagian Agregat Halus Pada Sifat Mekanik Paving Block. Mataram.
Hendra Purnomo, E. S 2014. Pemanfaatan Serbuk Kaca Sebagai Substitusi Parsial Semen Pada Campuran Beton Ditinjau Dari Kekuatan. Jurnal Fropil, 2.
Yohannes,dkk 2013. Kuat Tekan Beton Dengan Bahan Tambah Serbuk Kaca Sebagai Subtitusi Parsial Semen. Jurnal Sipil Statik Vol. 1 nomor 04.
Nugraha Sagit Sahay,dkk 2010. Penambahan Kawat Bendrat Pada Campuran Beton Terhadap Kuat Tekan Beton. Jurnal ISSN. Vol. 5 nomor 02.
Juwarnoko 2019. Pengaruh Penambahan Serat Kawat Bendrat Pada Campuran Beton Terhadap Kuat Tekan dan Kuat Tarik Beton. Semarang.
Kasno 2006. Pengaruh Penggunaan Potongan Kawat Bendrat Pada Campuran Beton.
Sudarmoko, & Sujatmiko. (2001). Pengaruh Konsentrasi Serat Baja Harex Terhadap Workabilitas, Kuat Tekan, Ketahanan Impak dan Abrasi Pada Beton. Jurnal Forum Teknik, 25(1), 40–51.
Suhendro. (1991). Pengaruh Fiber Kawat Pada Sifat-Sifat Beton, Seminar Mekanika Bahan Dalam Berbagai Aspek, Yogyakarta.
Nasional, B. S. (2004). Semen Portland. Dalam SNI 15-2049-2005.SNI
Nasional, B. S. (2000). Tata Cara Pembuatan Rencana Campuran Beton Normal. Dalam SNI 03-2834-1992.SNI
Nasional, B. S. (1996). Bata Beton (Paving Block). Dalam SNI 03-0691-1996. SNI.
Nasional, B. S. (2008). SNI 1970:2008 Cara Uji Berat Jenis dan Penyerapan Air Agregat Halus. Dalam SK SNI 03-1970-2008. SNI.
Nasional, B. S. (1989). Bata Beton Untuk Pasangan Dinding. Dalam SNI 03-0349-1989. SNI.
Nasional, B. S. (1996). Metoda pengujian Kuat Tekan Beton. Dalam SK SNI M–1–1989-F
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2022 Emerson Fitti Valdi
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
NHJ is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
Articles in this journal are Open Access articles published under the Creative Commons CC BY-NC-SA License This license permits use, distribution and reproduction in any medium for non-commercial purposes only, provided the original work and source is properly cited.
Any derivative of the original must be distributed under the same license as the original.